China Silicon carbide mirrors Manufacturers, Suppliers, Factory

SiC substrate can have microscopic defects, such as Threading Screw Dislocation (TSD), Threading Edge Dislocation (TED), Base Plane Dislocation (BPD), and others. These defects are caused by deviations in the arrangement of atoms at the atomic level. SiC crystals may also have macroscopic dislocations, like Si or C inclusions, micropipe, hexagonal voids, polymorphs, etc. These dislocations are typically large in size.

The coated parts in semiconductor silicon single crystal hot field are generally coated by CVD method, including pyrolytic carbon coating, Silicon Carbide coating and Tantalum Carbide coating, each with different characteristics.

Chemical Vapor Deposition (CVD) refers to a process technology where multiple gaseous reactants at varied partial pressures undergo a chemical reaction under specific temperature and pressure conditions. The resulting solid substance deposits on the surface of the substrate material, thereby obtaining the desired thin film. In traditional integrated circuit manufacturing processes, the obtained thin film materials are generally compounds such as oxides, nitrides, carbides, or materials like polycrystalline silicon, amorphous silicon, etc.

Currently, many semiconductor devices employ mesa device structures, which are predominantly created through two types of etching: wet etching and dry etching. While the simple and rapid wet etching plays a significant role in semiconductor device fabrication, it has inherent drawbacks such as isotropic etching and poor uniformity, which result in limited control when transferring small-sized patterns. Dry etching, however, with its high anisotropy, good uniformity, and repeatability, has become prominent in semiconductor device fabrication processes. The term “dry etching” broadly refers to any non-wet etching technology used for removing surface materials and transferring micro and nano patterns, including laser etching, plasma etching, and chemical vapor etching. The dry etching discussed in this text specifically pertains to the narrow application of processes using plasma discharge—either physical or chemical—to modify material surfaces.

The process of silicon carbide substrate is complex and difficult to manufacture. SiC substrate occupies the main value of the industry chain, accounting for 47%. It is expected that with the expansion of production capacity and the improvement of yield in the future, it is expected to drop to 30%.

At first glance, quartz (SiO2) material looks very similar to glass, but what is special is that ordinary glass is composed of many components (such as quartz sand, borax, boric acid, barite, barium carbonate, limestone, feldspar, soda ash, etc.), while quartz only contains SiO2, and its microstructure is a simple network composed of silicon dioxide tetrahedral structural units.